Éditeur(s) : HAL CCSD Royal Society of Chemistry
Résumé : International audience
A versatile sol-gel route has been developed for the preparation of hierarchical porous silica membrane material with highly dispersed platinum nanoparticles (Pt-NPs). The outstanding feature of the "one pot" synthesis developed in this work lies in the successful preparation of a stable complex suspension made of silica sol, multi-scale porogens and Pt nanoparticles. The multi-scale porogens were based on non-ionic triblock copolymers and aqueous latex suspension to create mesopores and macropores, respectively, with finely tuned pore size and organization. For further functionalization of the membranes, Pt nanoparticles of about 4 nm in diameter were prepared by irradiating with microwaves (MW) the Pt precursors added in the starting suspension. This original path is suggested to enable a pre-organization of Pt nanoparticles in the ordered mesoporous structure. The suspensions were then deposited as thin films on either dense or macroporous supports, and further thermally treated at 450°C to remove the porogen units. Hierarchical porous layers composed of micropores (<2 nm), ordered mesopores (∼4 nm) and macropores (∼70 nm) with or without Pt were prepared and characterized. The resulting membranes are foreseen to exhibit great potential as multifunctional membranes for gas separation coupled with catalytic reaction. © The Royal Society of Chemistry 2008.
ISSN: 0959-9428

hal-01680586
https://hal.univ-antilles.fr/hal-01680586
DOI : 10.1039/b807029f

Éditeur(s) : HAL CCSD Elsevier Masson
Résumé : International audience
Turbinaria turbinata brown seaweeds were tested as carbon electrode material in symmetric, electrochemical supercapacitors. The electrochemical properties of the carbon materials were characterised for their application as supercapacitors using cyclic voltammetry, galvanostatic charge/discharge method and electrochemical impedance spectroscopic analyses. Our initial results showed that the optimal behaviour was obtained for the sample prepared by pyrolysis at 800 degrees C. The average surface area of the carbon was 812 m(2)/g. Electrochemical tests with an organic electrolyte gave the following interesting results: a capacitance of 74.5 F/g, a specific series resistance of 0.5 Omega cm(2) and an ionic resistivity of 1.3 Omega cm(2). These results show the promising capacitive properties of carbon derived from seaweeds and their application in electrochemical supercapacitors. (C) 2013 Academie des sciences.
ISSN: 1631-0748

hal-00817880
http://hal.upmc.fr/hal-00817880
DOI : 10.1016/j.crci.2012.12.016