Éditeur(s) : HAL CCSD
Résumé : International audience
Alkaloids extract of Aspidosperma album was tested as corrosion inhibitor for C38 steel in 1 M HCl by using polarization and electrochemical impedance spectroscopy (EIS). Potentiodynamic polarization curves indicated that the plant extract behaves as mixed-type inhibitors. Impedance measurements showed that the double-layer capacitance decreased and charge-transfer resistance increased with increase in the inhibitors concentration and hence increasing in inhibition efficiency. The effect of temperature on the corrosion behavior of C38 steel in 1 M HCl with and without addition of plant extract was studied in the temperature range 25 – 55 °C. The adsorption of the inhibitor molecules was in accordance with the Langmuir adsorption isotherm. The results obtained show that this plant extract could serve as an effective inhibitor for the corrosion of C38 steel in hydrochloric acid.
International journal of electrochemical science

hal-01097107
https://hal-agroparistech.archives-ouvertes.fr/hal-01097107

Résumé : Ce travail porte sur l'inhibition de l'acier C38 en milieu acide HC1 1M par les extraits alcaloïdes issus de 2 plantes : aspidosperma album et geissospermum laeve. Biodégradables et respectueux de l'environnement, les alcaloïdes pourraient être utilisés temporairement pour prévenir la corrosion de l'acier C39 avec des taux d'inhibition supérieurs à ceux décrits dans la littérature. Dans la première partie du travail, l'influence de la concentration, du temps d'immersion et de la température sur le processus de corrosion de l'acier C38 en milieu HC1 1M en absence de polarisation et spectroscopie d'impédance électrochimique. Les analyses de surface effectuées par microscopie électronique a balayage montrent la présence d'une couche constituée d'un mélange d'oxyde de fer incorporant les alcaloïdes et qui conduit à la diminution de la vitesse de corrosion. La deuxième partie de ce travail a été consacrée à l'isolement des alcaloïdes des deux extraits afin de déterminer le ou les alcaloïdes responsables de l'activité inhibitrice et ainsi remonter aux mécanismes d’adsorption. Il a été montré que l'alcaloïde majoritaire des extraits est responsable de l'inhibition
This work is devoted to the corrosion inhibition of C38 steel in 1M HCL acid medium by alkaloids extracts from two plants : aspidosperma album and geissospermum laeve. Biodegradable and environmentally friendly, alkaloids could be used temporarily to prevent the corrosion of C38 steel with inhibition rates higher than those described in the literature. The first part of this work studies the influence of concentration, immersion time and temperature on the corrosion inhibitor by electrochemical measurements : polarization curves and electrochemical impedance spectroscopy. The surface analyses conducted by scanning electron microscopy showed the presence of a layer composed of an iron oxide mixture incorporating alkaloids extracts and which leads to the decrease of the corrosion rate. The second part of this work was devoted to the isolation of alkaloids of two extracts in order to determine the alkaloids responsible of the inhibitory activity and thus to determine the adsorption mechanisms. It was showed that the major alkaloids of two extracts is responsible of the inhibition activity

http://www.theses.fr/2013AGUY0578/document