Éditeur(s) : HAL CCSD
Résumé : International audience
In boundary lubrication regime, friction reduction and antiwear processes are associated to the presence of additives in the lubricating oils or greases. These processes are due to the formation of protective tribofilms resulting from chemical reactions between the additives and the sliding surfaces, in the physico-chemical conditions of the sliding contact. Conventional antiwear additives mainly consist of transition metal organo phosphate or thiophosphates which present a remarkable efficiency in the case of contacts between ferrous alloys. In the case of non reacting surfaces, these additives become inactive. Recently developped lubrication strategies consist in the use of dispersion in oils of nano additives able to build the protective tribofilm in the sliding contact without reaction with the surfaces. Carbon fluorinated phases, due to their lamellar structure and their high chemical stability even at relatively high temperature (400°C) represent interesting candidates as lubricant nano-additives subjected to present friction reduction, anti wear and anti corrosion actions. This work presents the tribologic behaviour of some carbon fluorinated derivatives such as graphite fluorides, fluorinated carbon nanofibers, fluorinated carbon nanodiscs and fluorinated carbon blacks. The influence, on the tribologic performances, of the structure of the initial carbon phases, of the fluorination rate (0
World Tribology Congress 2013
Torino, Italy

Droits : info:eu-repo/semantics/OpenAccess
hal-00926514
https://hal.archives-ouvertes.fr/hal-00926514
https://hal.archives-ouvertes.fr/hal-00926514/document
https://hal.archives-ouvertes.fr/hal-00926514/file/Delbe_9783.pdf
OATAO : 9783

Éditeur(s) : HAL CCSD ACS American Chemical Society - Publications
Résumé : International audience
ABSTRACT: In this paper, the structural, optical and thermal properties of n-type (100),p-type (100) and (111) mesoporous silicon (MePSi) are reported. The mesoporous silicon wasprepared by an electrochemical process from bulk silicon wafer. Depending on the etchingdepth, analyses show that the porosity of p-type (111) increased by 32 to 40% compared to p(100) which, in turn, increased by 22 to 48% compared to n-type (100). The structuremorphology and the abundance of Si-Ox and Si-Hy also depended heavily on the type andcrystal orientation of MePSi. The thermal properties of the MePSi layers such as thermalconductivity (κ), volumetric heat capacity (ρCp) and thermal contact resistance (Rth) weredetermined using the pulsed photothermal method. The thermal conductivity of bulk silicondropped sharply after etching, decreasing by more than twenty-fold in the case of n-type (100)and by over forty-five fold for p-type (100) and (111). According to the percolation modeldepending on both porosity and phonon confinement, the drop in thermal conductivity wasmainly due to the nanostructure formation after etching. Thermal investigations showed thatthe volumetric heat capacity (ρCp) followed the barycentric model which depends mainly onthe porosity. The thermal contact resistances of MePSi layers were estimated to be in therange of 1x10-8 to 1x10-7 K⋅m2⋅W-1.
The Journal of Physical Chemistry C

hal-01495490
https://hal.archives-ouvertes.fr/hal-01495490
DOI : 10.1021/acs.jpcc.6b13101

Éditeur(s) : HAL CCSD American Institute of Physics
Résumé : International audience
Laser-induced periodic surface structures (LIPSS) were formed on Cu/Si or Cu/glass thin films using Nd:YAG laser beam (40 ps, 10Hz, and 30mJ/cm2). The study of ablation threshold is always achieved over melting when the variation of the number of pulses increases from 1 to 1000. But the incubation effect is leading to reduce the threshold of melting as increasing the number of laser pulse. Also, real time reflectivity signals exhibit typical behavior to stress the formation of a liquid phase during the laser-processing regime and helps to determine the threshold of soft ablation.Atomic Force Microscopy (AFM) analyses have shown the topology of the micro-crater containing regular spikes with different height. Transmission Electron Microscopy (TEM) allows finally to show three distinguished zones in the close region of isolated protrusions. The central zone is a typical crystallized area of few nanometers surrounded by a mixed poly-crystalline and amorphous area. Finally, in the region far from the protrusion zone, Cu film shows an amorphous structure. The real time reflectivity, AFM, and HR-TEM analyses evidence the formation of a liquid phaseduring the LIPSS formation in the picosecond regime. VC 2015 AIP Publishing LLC
ISSN: 0003-6951

hal-01226065
https://hal.archives-ouvertes.fr/hal-01226065
DOI : 10.1063/1.4935413