Garnet growth in high-pressure, mafic garnet granulites formed by dehydration melting of hornblende-gabbronorite protoliths in the Jijal complex (Kohistan palaeo-island arc complex, north Pakistan) was investigated through a microstructural EBSD-SEM and HRTEM study. Composite samples preserve a sharp transition in which the low-pressure precursor is replaced by garnet through a millimetre-sized reaction front. A magmatic foliation in the gabbronorite is defined by mafic-rich layering, with an associated magmatic lineation defined by the shape-preferred orientation (SPO) of mafic clusters composed of orthopyroxene (Opx), clinopyroxene (Cpx), amphibole (Amp) and oxides. The shape of the reaction front is convoluted and oblique to the magmatic layering. Opx, Amp and, to a lesser extent, Cpx show a strong lattice-preferred orientation (LPO) characterized by an alignment of [001] axes parallel to the magmatic lineation in the precursor hornblende-gabbronorite. Product garnet (Grt) also displays a strong LPO. Two of the four < 111 > axes are within the magmatic foliation plane and the density maximum is subparallel to the precursor magmatic lineation. The crystallographic relationship < 111 >(Grt)//[001](Opx,Cpx,Amp) deduced from the LPO was confirmed by TEM observations. The sharp and discontinuous modal and compositional variations observed at the reaction front attest to the kinetic inhibition of prograde solid-state reactions predicted by equilibrium-phase diagrams. The P-T field for the equilibration of Jijal garnet granulites shows that the reaction affinities are 5-10 kJ mol.(-1) for the Grt-in reaction and 0-5 kJ mol.(-1) for the Opx-out reaction. Petrographic and textural observations indicate that garnet first nucleated on amphibole at the rims of mafic clusters; this topotactic replacement resulted in a strong LPO of garnet. Once the amphibole was consumed in the reaction, the parallelism of [001] axes of the mafic-phase reactants favoured the growth of garnet crystals with similar orientations over a pyroxene substrate. These aggregates eventually sintered into single-crystal garnet. In the absence of deformation, the orientation of mafic precursor phases conditioned the nucleation site and the crystallographic orientation of garnet because of topotaxial transformation reactions and homoepitaxial growth of garnet during the formation of high-pressure, mafic garnet-granulite after low-pressure mafic protoliths.
ISSN: 0263-4929

hal-00411323
https://hal.archives-ouvertes.fr/hal-00411323
DOI : 10.1111/J.1525-1314.2008.00789.x

Éditeur(s) : HAL CCSD Trans Tech Publications Inc.
Résumé : Two, high purity, Al-0.1 and 0.3wt%Mn alloys have been cold deformed in plane strain compression to strains of order 1.8 and the kinetics of subsequent recovery by sub-grain coarsening during annealing at 150-300°C measured by high resolution FEG-SEM EBSD. Accurate sub-grain size and misorientation distributions and their evolution with time and temperature have been determined. The average growth rates are then used to estimate the sub-grain boundary mobilities. Growth is analyzed by two well-known growth laws for the average sub-grain size δ (t): i) the standard relation for grain growth: where the exponent n takes values of 2-8 and ii) the relation proposed by Nes for dislocation climb in sub-grain walls: It is shown that the latter relation gives a better fit with the data in terms of the time and temperature dependence of the sub-grain sizes. In particular the activation energies for the logarithmic law are much closer to the values expected for solute-controlled movement of sub-boundaries.
Materials Science Forum

hal-00795441
https://hal.archives-ouvertes.fr/hal-00795441
DOI : 10.4028/www.scientific.net/MSF.715-716.725

Éditeur(s) : HAL CCSD
Résumé : International audience
The influence of Mn solute atoms on sub-grain boundary mobilities in Al has been determined by accurate electron backscatter diffraction analysis of the sub-grain sizes and misorientations during recovery annealing. High purity Al-0.1 and 0.3 wt.% Mn alloys were deformed by plane strain compression at room temperature to equivalent strains of 1.8 and annealed in the temperature range 150-300 °C. An original method of image analysis on sub-boundaries from electron backscatter diffraction maps was applied to quantify the sub-grain size distributions. The change in average sub-grain size with time at several temperatures was then used to estimate sub-grain boundary mobilities in both Al-Mn alloys. The activation energies for sub-grain mobility were found to be 48 and 52 and kJ.mol^-1 for the 0.1 and 0.3 % Mn alloys respectively, with the higher Mn alloy exhibiting lower rates. The sub-boundary mobilities are higher than expected from previous similar work on deformed Al-Si crystals. The orientation dependence of sub-grain growth is also examined.
International Journal of Materials Research

emse-00463551
https://hal-emse.ccsd.cnrs.fr/emse-00463551
DOI : 10.3139/146.110057