Éditeur(s) : HAL CCSD
Résumé : In order to minimize CO2 atmospheric concentration, a solution consists in sequestrating CO2 in geological reservoirs. To estimate long term risks, it is necessary to quantify the couplings between reaction processes as well as structural and hydrodynamical modifications. We realised two experimental benches enabling injecting CO2-enriched-brine in conditions corresponding to in situ storage (T < 200 oC and P < 200 bar) and developed
an experimental protocol using X-Ray microtomography and fluid and rock analyses in order to measure the variations of physical and chemical parameters.
The study of carbonated reservoirs near the injection well, allows quantifying different k-phi relationships depending on the dissolution processes and triggered by the local fluid chemical composition and initials conditions. Away from the injection well, we observe carbonate precipitation decreasing the permeability. The study of fracturated caprock samples shows that alternative percolation of CO2-enriched-brine and CO2 gas increases the fracture permeability.
The study of silicated rocks indicates carbonate precipitation in zeolite sandstone and sintered dunite grains. Nevertheless, in zeolite sandstone we also observe the precipitation of clay particles located in the uid pathways which decrease strongly the permeability.
Afin de minimiser la concentration en CO2 dans l'atmosphère une solution consiste à le séquestrer dans les réservoirs géologiques. Pour évaluer les risques à long terme, il est nécessaire de quantifier les couplages entre les processus réactionnels et les modifications structurales et hydrodynamiques. Dans cette optique, nous avons construit deux dispositifs expérimentaux permettant d'injecter des saumures chargées en CO2 dans les conditions de stockage (T < 200 °C et P < 200 bar) et mis en oeuvre un protocole expérimental utilisant la microtomographie RX et l'analyse des roches et des fuides pour quantifier les variations des paramètres physiques et chimiques. Dans le cas des réservoirs carbonatés, on observe, près du puits d'injection, une forte variabilité des relations k-phi en fonction du régime de dissolution contrôlé par la chimie locale du fluide, ainsi que par les conditions initiales. A plus grande distance, on observe des processus de précipitation diminuant fortement la perméabilité. L'étude des roches de couverture fracturées (argilite) a montré qu'une percolation alternée d'une saumure chargée en CO2 et de CO2 gaz augmentait la perméabilité de fracture. Dans le cas des roches silicatées, la précipitation de carbonates est mise en évidence aussi bien dans les grès à zéolites que dans les frittés de dunite de San Carlos. Cependant, dans les grès à zéolites, la précipitation d'une phase argileuse est observée dans les chemins d'écoulement et engendre une forte diminution de la perméabilité.
https://tel.archives-ouvertes.fr/tel-00416408

tel-00416408
https://tel.archives-ouvertes.fr/tel-00416408
https://tel.archives-ouvertes.fr/tel-00416408/document
https://tel.archives-ouvertes.fr/tel-00416408/file/These_Luquot.pdf

Éditeur(s) : HAL CCSD
Résumé : The main purpose of this thesis was to characterize and to model the hydrodynamic and thermochemical processes leading to the alteration of the wellbore cement materials under borehole conditions. Percolation experiments were performed on fractured cement samples under CO2 storage conditions (60°C and 10MPa). Injection flow rate was dictated by the fracture aperture of each sample. CO2 enriched brine was flowed along the fracture aperture, and permeability changes as well as chemical evolution of major cations were continuously acquired during the experiment time. Reaction paths developed by the alteration of the cement were characterized using microtomography and ESEM images. The experiments conducted using samples presenting large fracture apertures during 5h showed that permeability was maintained constant during the experiment time. Three reacted layers were displaying by the alteration of portlandite and CSH. Long term experiment (26h) conducted with large initial fracture aperture showed a decrease of the permeability after 15hours of CO2 exposure. Otherwise, experiments performed on samples presenting narrow apertures indicated the conversion of portlandite and CSH to calcite leading to the permeability reduction and the fracture clogging. Assemblages of phases and chemical changes were modelled using GEMS-PSI speciation code. We studied also using a coupled transport-reactive model the conditions leading to the cement alteration and the formation of associated layers.
L'objectif de cette thèse était de modéliser à partir des expériences de percolation-réactive, les processus hydrodynamique et réactionnel qui gouvernent l'altération des ciments de puits. Différentes expériences ont été réalisées dans des conditions représentatives de celles du stockage du CO2. Des échantillons fracturés ont été utilisés pour injecter une saumure enrichie en CO2 à 60°C et 10MPa et à différentes pressions partielles de CO2. Le débitd'injection variait en fonction des propriétés hydrauliques de l'échantillon exposé. L'injection d'une saumure enrichie en CO2 à débit constant à travers une fracture supposée plane a permis d'étudier les modifications des propriétés hydrodynamiques et ces conséquences sur la géochimie et la microstructure du ciment altéré. L'impact dynamique de l'évolution microstructurale a été mis en évidence. Les expériences conduites sur des échantillons présentant de larges ouvertures, réalisées sur une durée de 5 h, ont montré que la perméabilité était maintenue constante le long de l'expérience. Trois couches d'altération se sont développées consécutivement à la dissolution de la portlandite et la décalcification des CSH. L'altération a entrainé la précipitation des carbonates et de la silice amorphe à proximité de la fracture. Dans le cas d'une expérience longue durée appliquant les mêmes conditions que précédemment on a observé que la croissance de la silice amorphe a entrainé la diminution de la perméabilité. Par ailleurs les expériences effectuées sur des échantillons présentant de faibles ouvertures, ont indiqué que la conversion de la portlandite en calcite conduit au colmatage de la fracture. L'évolution des assemblages de phases conduisant à la formation des carbonates et de la silice amorphe a été modélisée à partir du code géochimique GEMS. Les mécanismes de diffusion et les processus de mise en place des couches d'altération ont été étudiés à partir d'un modèle analytique et d'un modèle de transport réactif à partir du code géochimique PHREEQC.
https://tel.archives-ouvertes.fr/tel-01038034

tel-01038034
https://tel.archives-ouvertes.fr/tel-01038034
https://tel.archives-ouvertes.fr/tel-01038034/document
https://tel.archives-ouvertes.fr/tel-01038034/file/theseabdoulghafour.pdf