Éditeur(s) : HAL CCSD American Chemical Society
Résumé : Experiments were conducted to assess the potential impact of fractured well-cement degradation on leakage rate. Permeability was monitored while CO2-enriched reservoir-equilibrated brine was flowed at constant rate through a single fracture in a class G cement core under conditions mimicking geologic sequestration environments (temperature 60 °C, pressure 10 MPa). The results demonstrate that, at least for the conditions used in the experiment, an initial leakage in a 42 μm aperture fracture (permeability = 1.5 × 10-10 m2) can be self-mitigated due to the decrease of the fracture hydraulic aperture after about 15 h. This decrease results from the development of continuous highly hydrated amorphous Si-rich alteration products at the edge of the fracture and the dense carbonation of the bulk cement that mitigate the penetration of the alteration front.
ISSN: 0013-936X

hal-00950088
https://hal.archives-ouvertes.fr/hal-00950088
DOI : 10.1021/es401317c

Éditeur(s) : HAL CCSD Elsevier
Résumé : Deficient sealing in the well cement plugs and annulus due to mechanical fracturing is an important risk of CO2 leakage from the reservoir to others permeable layers and the surface. Such situation was reproduced at laboratory scale in order to determine the hydro-chemical control on the fracture permeability. Specifically, we investigated the effect of CO2 rich-brine flowing through fractured Portland cements at T = 60 °C and P = 10 MPa and variable flow rates. We showed that carbonation process is dominant and induces permeability decrease and leakage mitigation for extremely low flow rate whereas for high flow rate injection the permeability remains constant due to the precipitation of a low density secondary Si-rich phase which maintains the initial fracture aperture. At intermediate flow rate the hydraulic aperture can increase due to the densification of the material triggered by the net precipitation of low porosity calcite. These results emphasize that more complex behaviors than those considered from batch experiments may take place in the vicinity of flowing fractures. Specifically, the redissolution of the neoformed calcite as well as the development of amorphous phases, both controlled by the CO2-rich brine renewing rate in the fracture may prevent the healing fracture.
ISSN: 1750-5836

hal-00857555
https://hal.archives-ouvertes.fr/hal-00857555
DOI : 10.1016/j.ijggc.2013.04.002

Éditeur(s) : HAL CCSD Elsevier
Résumé : Adequate hydrogeophysical monitoring of CO2 geological storage remains a challenge as different parameters might be modified during storage. That implies to compare real-time measurements to an adequate baseline. At the Maguelone shallow experimental site a representative baseline for electrical resistivity was built from a large number of downhole geophysical measurements. At this coastal site this issue is particularly important due to the production of biogenic gas from the subsurface sediments. For this, a modified petrophysical model based on the Waxman-Smits model is proposed to estimate gas saturation found to vary from 2 to 7% within shallow sand layers.
ISSN: 1876-6102

hal-01412685
https://hal.archives-ouvertes.fr/hal-01412685
https://hal.archives-ouvertes.fr/hal-01412685/document
https://hal.archives-ouvertes.fr/hal-01412685/file/pezard2015.pdf
DOI : 10.1016/j.egypro.2015.07.910

Éditeur(s) : HAL CCSD Elsevier
Résumé : We investigate experimentally the alteration of fractured class-G cement flowed by CO2-rich brine. The experiment mimics a mechanically damaged rough-walled fractured cement annulus at temperature 60 °C and pressure 10 MPa. The experiment consists of flowing a reservoir-equilibrated brine mixed with CO2 (partial pressure of 2.3 MPa) through the fracture of average aperture 14 μm at constant flow rate (100 μL min−1). This flow rate corresponds to pressure gradient representative of an average in situ hydrodynamic condition. Results indicate an intense alteration of the cement with a large removal of mass at the scale of the sample. However, the fracture alteration patterns are triggered by the initial heterogeneity of the fracture aperture; the aperture of the low aperture zones tends to decrease due to calcite precipitation whereas preferential paths develop in the zones of higher aperture associated. Nevertheless, the expected large permeability increase triggered by the mass removal is mitigated by the precipitation of a low density Si-rich amorphous material. The alteration rate will decrease with time because of the increasing distance of diffusion between the fracture where the reactants are actively renewed by advection and the portlandite and C-S-H dissolution fronts. The different zones of reaction can be adequately modeled by a simple 1D diffusion-reaction model using published kinetics coefficients and extrapolation to larger times than the experiment time can be drawn. Altogether, and in addition to the previous studies of the alteration of fractured well cement annulus, this study shows that the leakage potential is strongly controlled by the initial distribution of the aperture along the fracture: low aperture zones will tend to self-heal while localized flow in connected high aperture paths will be perennial.
ISSN: 1750-5836

hal-01346006
https://hal.archives-ouvertes.fr/hal-01346006
DOI : 10.1016/j.ijggc.2016.01.032

Éditeur(s) : HAL CCSD
Résumé : The main purpose of this thesis was to characterize and to model the hydrodynamic and thermochemical processes leading to the alteration of the wellbore cement materials under borehole conditions. Percolation experiments were performed on fractured cement samples under CO2 storage conditions (60°C and 10MPa). Injection flow rate was dictated by the fracture aperture of each sample. CO2 enriched brine was flowed along the fracture aperture, and permeability changes as well as chemical evolution of major cations were continuously acquired during the experiment time. Reaction paths developed by the alteration of the cement were characterized using microtomography and ESEM images. The experiments conducted using samples presenting large fracture apertures during 5h showed that permeability was maintained constant during the experiment time. Three reacted layers were displaying by the alteration of portlandite and CSH. Long term experiment (26h) conducted with large initial fracture aperture showed a decrease of the permeability after 15hours of CO2 exposure. Otherwise, experiments performed on samples presenting narrow apertures indicated the conversion of portlandite and CSH to calcite leading to the permeability reduction and the fracture clogging. Assemblages of phases and chemical changes were modelled using GEMS-PSI speciation code. We studied also using a coupled transport-reactive model the conditions leading to the cement alteration and the formation of associated layers.
L'objectif de cette thèse était de modéliser à partir des expériences de percolation-réactive, les processus hydrodynamique et réactionnel qui gouvernent l'altération des ciments de puits. Différentes expériences ont été réalisées dans des conditions représentatives de celles du stockage du CO2. Des échantillons fracturés ont été utilisés pour injecter une saumure enrichie en CO2 à 60°C et 10MPa et à différentes pressions partielles de CO2. Le débitd'injection variait en fonction des propriétés hydrauliques de l'échantillon exposé. L'injection d'une saumure enrichie en CO2 à débit constant à travers une fracture supposée plane a permis d'étudier les modifications des propriétés hydrodynamiques et ces conséquences sur la géochimie et la microstructure du ciment altéré. L'impact dynamique de l'évolution microstructurale a été mis en évidence. Les expériences conduites sur des échantillons présentant de larges ouvertures, réalisées sur une durée de 5 h, ont montré que la perméabilité était maintenue constante le long de l'expérience. Trois couches d'altération se sont développées consécutivement à la dissolution de la portlandite et la décalcification des CSH. L'altération a entrainé la précipitation des carbonates et de la silice amorphe à proximité de la fracture. Dans le cas d'une expérience longue durée appliquant les mêmes conditions que précédemment on a observé que la croissance de la silice amorphe a entrainé la diminution de la perméabilité. Par ailleurs les expériences effectuées sur des échantillons présentant de faibles ouvertures, ont indiqué que la conversion de la portlandite en calcite conduit au colmatage de la fracture. L'évolution des assemblages de phases conduisant à la formation des carbonates et de la silice amorphe a été modélisée à partir du code géochimique GEMS. Les mécanismes de diffusion et les processus de mise en place des couches d'altération ont été étudiés à partir d'un modèle analytique et d'un modèle de transport réactif à partir du code géochimique PHREEQC.
https://tel.archives-ouvertes.fr/tel-01038034

tel-01038034
https://tel.archives-ouvertes.fr/tel-01038034
https://tel.archives-ouvertes.fr/tel-01038034/document
https://tel.archives-ouvertes.fr/tel-01038034/file/theseabdoulghafour.pdf