Éditeur(s) : HAL CCSD
Résumé : International audience
In this work, a series of zinc partially substituted magnetite nanoparticles (Fe3-xZnxO4, 0 ≤ x ≤ 0.4), were synthesised through a facile precipitation-oxidation method. The partial substitution of zinc into the magnetite (Fe3O4) structure was confirmed by the collective findings of nitrogen sorption, XRD and TG-DTG analysis. It was found that the partial substitution of zinc slightly changed the textural properties of the resultant Fe3-xZnxO4 nanoparticles. From the XRD analysis, there was no visible formation of secondary phase or impurity peaks in the nanoparticles. These findings indicated the partial substitution of zinc into the Fe3O4 crystal structure with a good dispersion within the Fe3O4 matrix. © 2016 Author(s).
1st International Conference on Advanced Science,
Penang, Malaysia

hal-01683217
https://hal.univ-antilles.fr/hal-01683217

Éditeur(s) : HAL CCSD Elsevier
Résumé : International audience
Here we show that copper substitution in perovskite-type barium strontium cobalt copper oxide (BSCC) membranes confers extremely high oxygen fluxes well beyond the state of art, reaching 27.5 ml cm−2 min−1at 950 °C. A key feature of BSCC is the formation of a mixed matrix catalyst-perovskite membrane caused by the segregation of copper, leading to the formation of an intergranular network of copper-rich oxide between perovskite grains. BSCC membranes delivered pressure normalised oxygen flux (i.e. permeance) of up to 86 times higher, above pressure difference of 18 kPa, as compared to best perovskite membrane, BBSC, due to the catalytic effect of segregated copper oxide. Unlike conventional dual-phase membranes which contain ion and electron conducting phases, this work shows for the first time perovskite-type membranes consisting of a mixed matrix of oxygen ion/electron conducting (perovskite) and catalytic (copper oxide) phases, thus paving the way to the development of high performance membranes for oxygen separation from air for clean energy applications. © 2016 Elsevier B.V.
ISSN: 0376-7388

hal-01683219
https://hal.univ-antilles.fr/hal-01683219
DOI : 10.1016/j.memsci.2016.12.035

Éditeur(s) : HAL CCSD Elsevier
Résumé : International audience
This work shows the preparation and separation performance assessment of carbon membranes derived from phenolic resin by a vacuum-assisted method and carbonisation in an inert atmosphere. The vacuum time played an important role in tailoring the structure of the membranes. For instance, pore volumes and surface areas increased from 0.81 and 834 to 2.2 cm3g−1and 1910 m2g−1, respectively, as the vacuum time exposure increased from 0 to 1200 s. The significant structural changes correlated very well with water permeation, as fluxes increased by 91% as the vacuum time increased from 0 to 1200 s reaching up to 169 L m−2h−1at 5 bar. Molecular weight cut-off tests showed no rejection for the smaller glucose and sucrose molecules, though this increased to ~ 80% and full rejection for 36 kDa and 400 kDa polyvinyl pyrrolidine. Interestingly, FTIR spectra showed that the peaks of C–H stretching vibration (2800–3200 cm−1) and C–O stretching (1030 cm−1) became more pronounced as a function of increasing vacuum time, strongly suggesting that the use of vacuum further assisted in the polycondensation of phenolic oligomers. Based on these outcomes, a cluster to cluster model is proposed, whereby vacuum application promoted crosslinking reactions of the phenolic resin, creating microporous regions within the clusters, and mesoporous regions between the clusters. © 2016 Elsevier B.V
ISSN: 0376-7388

hal-01683220
https://hal.univ-antilles.fr/hal-01683220
DOI : 10.1016/j.memsci.2016.11.002

Éditeur(s) : HAL CCSD Royal Society of Chemistry
Résumé : International audience
Owing to the electron donor-acceptor properties of GO, the active sites (≡Fe2+) of Fe3O4 are not oxidised (≡Fe3+) in the heterogeneous Fenton-like reaction. GO plays a sacrificial role via the oxidation of (C=C) carbon domains, and transferring electrons to Fe3O4. Therefore, GO-Fe3O4 confers superior catalytic efficiency, recyclability and longevity, otherwise not available in Fe3O4. © The Royal Society of Chemistry 2015.
ISSN: 1359-7345

hal-01683211
https://hal.univ-antilles.fr/hal-01683211
DOI : 10.1039/c5cc02292d

Éditeur(s) : HAL CCSD Elsevier
Résumé : International audience
Mesoporous cobalt oxide silica matrices and membranes were successfully prepared using a dual acid-base catalysed sol-gel and interlayer-free approach for desalination applications. The effects of cobalt addition (0-35 mol%) on the structure-property relationship of the silica materials and membrane performance were systematically studied as a function of feed salt concentration (0.3-7.5 wt.% NaCl) and temperature (22-60 °C). As cobalt concentration increases beyond 5 mol%, the concentration of tricobalt tetroxide and proportion of silica mesopores were found to increase within the matrices. Silica membranes with high amount of tricobalt tetroxide (35 mol%) were found to be highly mesoporous with water fluxes of 20, 11.3 and 7.7 kg m-2 h-1 for the 0.3, 3.5 and 7.5 wt.% solutions at 60 °C, respectively, with >99.7% salt rejection at all times. This is attributed to the high pore volume (mesopores formation) and structural robustness of the silica network provided by the presence of tricobalt tetroxide. Even higher performance was achieved for low tricobalt tetroxide (mol%) silica membranes with water fluxes of 47.6 (0.3 wt.%) and 31.5 (3.5 wt.%) kg m-2 h-1 at 60 °C, respectively, though with reduced salt rejections of 90%. © 2015 Elsevier B.V.
ISSN: 0011-9164

hal-01683209
https://hal.univ-antilles.fr/hal-01683209
DOI : 10.1016/j.desal.2015.02.034

Éditeur(s) : HAL CCSD MDPI
Résumé : International audience
This work investigates the structural formation and analyses of titania membranes (TM) prepared using different vacuum exposure times for molecular weight (MW) cut-off performance and oil/water separation. Titania membranes were synthesized via a sol-gel method and coated on macroporous alumina tubes followed by exposure to a vacuum between 30 and 1200 s and then calcined at 400 °C. X-ray diffraction and nitrogen adsorption analyses showed that the crystallite size and particle size of titania increased as a function of vacuum time. All the TM membranes were mesoporous with an average pore diameter of ~3.6 nm with an anatase crystal morphology. Water, glucose, sucrose, and polyvinylpyrrolidone with 40 and 360 kDa (PVP-40 kDa and PVP-360 kDa) were used as feed solutions for MW cut-off and hexadecane solution for oil filtration investigation. The TM membranes were not able to separate glucose and sucrose, thus indicating the membrane pore sizes are larger than the kinetic diameter of sucrose of 0.9 nm, irrespective of vacuum exposure time. They also showed only moderate rejection (20%) of the smaller PVP-40 kDa, however, all the membranes were able to obtain an excellent rejection of near 100% for the larger PVP-360 kDa molecule. Furthermore, the TM membranes were tested for the separation of oil emulsions with a high concentration of oil (3000 ppm), reaching high oil rejections of more than 90% of oil. In general, the water fluxes increased with the vacuum exposure time indicating a pore structural tailoring effect. It is therefore proposed that a mechanism of pore size tailoring was formed by an interconnected network of Ti-O-Ti nanoparticles with inter-particle voids, which increased as TiO2 nanoparticle size increased as a function of vacuum exposure time, and thus reduced the water transport resistance through the TM membranes. © 2016 by the authors.
ISSN: 1996-1944

hal-01683214
https://hal.univ-antilles.fr/hal-01683214
DOI : 10.3390/ma9110938

Éditeur(s) : HAL CCSD Nature Publishing Group
Résumé : International audience
Abstract View references (45)Graphene oxide-iron oxide (GO-Fe3O4) nanocomposites were synthesised by co-precipitating iron salts onto GO sheets in basic solution. The results showed that formation of two distinct structures was dependent upon the GO loading. The first structure corresponds to a low GO loading up to 10wt%, associated with the beneficial intercalation of GO within Fe3O4nanoparticles and resulting in higher surface area up to 409m2g-1. High GO loading beyond 10 wt% led to the aggregation of Fe3O4 nanoparticles and the undesirable stacking of GO sheets. The presence of strong interfacial interactions (Fe-O-C bonds) between both components at low GO loading lead to 20% higher degradation of Acid Orange 7 than the Fe3O4 nanoparticles in heterogeneous Fenton-like reaction. This behaviour was attributed to synergistic structural and functional effect of the combined GO and Fe3O4 nanoparticles.
ISSN: 2045-2322

hal-01683208
https://hal.univ-antilles.fr/hal-01683208
DOI : 10.1038/srep04594

Éditeur(s) : HAL CCSD Royal Society of Chemistry
Résumé : International audience
A series of graphene oxide (GO) and zinc partially substituted magnetite GO-Fe1-xZnxOy (0 ≤ x ≤ 0.285) catalysts were synthesised through a precipitation-oxidation method. The rate constants for the degradation of acid orange seven (AO7) proceeded at a significant faster rate under UV-irradiation (up to 670%) than the conventional heterogeneous Fenton-like reaction. The resultant catalysts were mesoporous, so there was no mass transfer limitation for AO7 to access active sites in the catalysts. Further, maximum increases of rate constant up to 220% occurred as the zinc molar concentration increased from x = 0 to x = 0.159. GO enhanced to incorporation of zinc into the combined metal oxide, whilst zinc limited crystal growth, thus forming smaller crystallite sizes. These features proved to be essential for the improved catalytic activity of the resultant catalysts. The optimised zinc molar value at x = 0.159 delivered the best catalytic activity. © The Royal Society of Chemistry 2016.
ISSN: 2046-2069

hal-01683215
https://hal.univ-antilles.fr/hal-01683215
DOI : 10.1039/c6ra04068c

Éditeur(s) : HAL CCSD Elsevier
Résumé : International audience
Abstract View references (38)Silicalite-1 (S-1) and ZSM-5 membranes prepared by secondary growth on tubular ceramic supports were tested using a pervaporation set up for the desalination of aqueous solutions containing NaCl in concentrations corresponding to brackish (0.3-1wt%), sea (3.5wt%) and brine (7.5-15wt%) water. ZSM-5 membranes delivered higher water fluxes when compared with S-1 membranes due to enhanced hydrophilicity of the Al-rich zeolite structure leading to fluxes as high as 11.5kgm -2h -1 for 0.3wt% NaCl feed solutions at 75°C. At higher salt concentration the water flux decreased alongside with the salt rejection rate, however the hydrophilic ZMS-5 membrane became more susceptible to performance loss, particularly at high temperatures. Detailed stability experiments carried out for up to 560h showed the dissolution of both S-1 and ZSM-5 top layers. This was attributed to the combined effects of ion exchange and water dissolution mechanisms. Interesting though, the MFI structure zeolite was still observed on the XRD patterns whilst EDX depth profile showed the presence of silica up to 30μm depth into the support. These results suggest the formation/infiltration of a compact amorphous phase in the substrate, derived from the aggregation of the dissolved silicate species and possibly together with the arrangement of MFI nano-slabs during the desalination tests. Despite generating lower water fluxes, the S-1 membrane exhibited relatively high robustness under the long term testing conditions which included temperature cycling, delivering salt rejections from initial >99% to <80% at the end of the testing period (560h). © 2012 Elsevier B.V.
ISSN: 0376-7388

hal-01683201
https://hal.univ-antilles.fr/hal-01683201
DOI : 10.1016/j.memsci.2012.05.074